Nanocrystalline Composite Layer Realized by Simple Sintering Without Surface Treatment, Reducing Hydrophilicity and Increasing Thermal Conductivity.

The surface treatment for a polymer-ceramic composite is additionally performed in advanced material industries. To prepare the composite without a surface treatment, the simplest way to manufacture an advanced ceramic-particle is devised. The method is the formation of a nanocrystalline composite layer through the simple liquid-phase sintering. Using magnesia (MgO) which shows hydrophilicity, a nanocrystalline surface layer is realized by liquid-phase sintering. The amorphous matrix of nanocrystalline composite layer makes MgO hydrophobic and ensures miscibility with polymers, and the nanocrystalline MgO ensures high thermal conductivity. In addition, the liquid phase removes the open pores and makes the surface morphology smooth MgO with smooth surface (MgO-SM). Thermal interface materials (TIM) prepared with MgO-SM and epoxy show a high thermal conductivity of ≈7.5 W m-1 K-1 , which is significantly higher than 4.5 W m-1 K-1 of pure MgO TIM. Consequently, the formation process of a nanocrystalline surface layer utilizing simple liquid-phase sintering is proposed as a fabrication method for a next-generation ceramic-filler. In addition, it is fundamentally identified that the thermal conductivity of MgO depends on the Mg deficiency, and therefore a poly-crystal MgO-SM (produced at a low temperature) has a higher thermal conductivity than a single-crystal MgO (produced at a high temperature).

Effect of Cathode Microstructure on Electrochemical Properties of Sodium Nickel-Iron Chloride Batteries.

Sodium metal chloride batteries have become a substantial focus area in the research on prospective alternatives for battery energy storage systems (BESSs) since they are more stable than lithium ion batteries. This study demonstrates the effects of the cathode microstructure on the electrochemical properties of sodium metal chloride cells. The cathode powder is manufactured in the form of granules composed of a metal active material and NaCl, and the ionic conductivity is attained by filling the interiors of the granules with a second electrolyte (NaAlCl4). Thus, the microstructure of the cathode powder had to be optimized to ensure that the second electrolyte effectively penetrated the cathode granules. The microstructure was modified by selecting the NaCl size and density of the cathode granules, and the resulting Na/(Ni,Fe)Cl2 cell showed a high capacity of 224 mAh g-1 at the 100th cycle owing to microstructural improvements. These findings demonstrate that control of the cathode microstructure is essential when cathode powders are used to manufacture sodium metal chloride batteries.